Crystal size | ~10 mm |
Electrical properties | Metal, Superconductor (Tc~7.2K), Charge Density Waves (CDW) system, Tcdw ~33K |
Crystal structure | hexagonal |
Unit cell parameters | a = b = 0.344 nm, c = 1.255 nm, α = β = 90°, γ = 120° |
Type | Synthetic |
Purity | >99.995 % |
Characterized by | XRD, Raman, EDX |
More information? | Please contact us by email or phone |
XRD: single crystal and powder X-ray diffraction (D8 Venture Bruker and D8 Advance Bruker)
EDX: Energy-dispersive X-ray spectroscopy for stoichiometric analysis
Raman: 785 nm Raman system
Click on an image to zoom
X-ray diffraction on a 2H phase NbSe2 single crystal aligned along the (001) plane. XRD was performed at room temperature using a D8 Venture Bruker. The 4 XRD peaks correspond, from left to right, to (00l) with l = 2, 4, 6, 8
Powder X-ray diffraction (XRD) of a single crystal 2H NbSe2. X-ray diffraction was performed at room temperature using a D8 Venture Bruker.
Stoichiometric analysis of a single crystal 2H NbSe2 by Energy-dispersive X-ray spectroscopy (EDX).
Raman spectrum of a single crystal 2H NbSe2. Measurement was performed with a 785 nm Raman system at room temperature.
1. Naoto Yabuki et al., "Supercurrent in van der Waals Josephson junction",Nature Communications 7, 10616 (2016), link to article:
http://www.nature.com/ncomms/2016/160202/ncomms10616/full/ncomms10616.html?WT.ec_id=NCOMMS-20160205
2. Y. Cao et al., "Quality Heterostructures from Two-Dimensional Crystals Unstable in Air by Their Assembly in Inert Atmosphere", Nano Lett. 15 (8), 4914-4921 (2015), link to article:
http://pubs.acs.org/doi/abs/10.1021/acs.nanolett.5b00648